Technological measures for reducing deformation in processing aluminum parts

2023-01-06(3627)Views

1、 Technological measures to reduce processing deformation 1. Reduce the internal stress of the blank. Natural or artificial aging and vibration treatment can partially eliminate the internal stress of the blank. Pre-processing is also an effective process method. For the rough of fat head and big ears, due to the large margin, the deformation after processing is also large. If the surplus parts of the blank are processed in advance and the allowance of each part is reduced, not only can the processing deformation of the subsequent processes be reduced, but also a part of the internal stress can be released after the pre-processing is placed for a period of time. 2. To improve the cutting ability of the tool, the material and geometric parameters of the tool have an important impact on the cutting force and cutting heat. The correct selection of the tool is essential to reduce the machining deformation of the part. 1) Reasonable selection of tool geometric parameters. ① Front angle: under the condition of maintaining the strength of the blade, the front angle should be appropriately larger, one side
1、 Technological measures to reduce processing deformation
1. Reduce the internal stress of the blank
Natural or artificial aging and vibration treatment can partially eliminate the internal stress of the blank. Pre-processing is also an effective process method. For the rough of fat head and big ears, due to the large margin, the deformation after processing is also large. If the surplus parts of the blank are processed in advance and the allowance of each part is reduced, not only can the processing deformation of the subsequent processes be reduced, but also a part of the internal stress can be released after the pre-processing is placed for a period of time.

2. Improve the cutting ability of the tool
The material and geometric parameters of the tool have an important impact on the cutting force and cutting heat. The correct selection of the tool is crucial to reduce the machining deformation of the part.
1) Reasonable selection of tool geometric parameters.
① Front angle: under the condition of maintaining the strength of the cutting edge, the front angle should be appropriately larger. On the one hand, it can grind the sharp edge, and on the other hand, it can reduce the cutting deformation, make the chip removal smooth, and then reduce the cutting force and cutting temperature. Never use negative rake tools.
② Back angle: The size of the back angle has a direct impact on the wear of the back tool surface and the quality of the machined surface. Cutting thickness is an important condition for selecting back angle. During rough milling, due to the large feed rate, heavy cutting load and large heat generation, the tool heat dissipation condition is required to be good, so the back angle should be smaller. During finishing milling, the cutting edge is required to be sharp to reduce the friction between the back face and the machined surface and reduce the elastic deformation. Therefore, the back angle should be larger.
③ Helical angle: In order to make milling smooth and reduce milling force, the spiral angle should be selected as large as possible.
④ Main deflection angle: properly reducing the main deflection angle can improve the heat dissipation conditions and reduce the average temperature of the processing area.

2) Improve tool structure.
① Reduce the number of milling cutter teeth and increase the chip holding space. Due to the large plasticity of aluminum parts and the large cutting deformation during machining, large chip holding space is required, so the radius of the chip holding groove bottom should be larger and the number of milling cutter teeth should be smaller.
② Finish grinding cutter teeth. The roughness value of the cutting edge of the cutter tooth should be less than Ra=0.4um. Before using a new knife, gently grind the front and back of the knife tooth with a fine oilstone to remove the remaining burrs and slight serrations when grinding the knife tooth. In this way, not only cutting heat can be reduced, but also cutting deformation is relatively small.
③ Strictly control the tool wear standard. After tool wear, the workpiece surface roughness value increases, the cutting temperature increases, and the workpiece deformation increases. Therefore, in addition to selecting the tool material with good wear resistance, the tool wear standard should not be greater than 0.2mm, otherwise it is easy to produce chips. During cutting, the temperature of the workpiece should not exceed 100 ℃ to prevent deformation.

3. Improve the clamping method of workpiece
For thin-walled aluminum parts with poor rigidity, the following clamping methods can be used to reduce deformation:
① For thin-walled bushing parts, if the three-jaw self-centering chuck or spring chuck is used to clamp radially, the workpiece will inevitably deform once it is loosened after processing. At this time, the method of axial end compression with good rigidity should be used. Position with the inner hole of the part, make a threaded mandrel, insert it into the inner hole of the part, press the end face with a cover plate and then back it with a nut. The clamping deformation can be avoided when machining the outer circle, so as to obtain satisfactory machining accuracy.
② When processing thin-walled thin plate workpiece, it is best to select vacuum chuck to obtain evenly distributed clamping force, and then use small cutting amount to process, which can effectively prevent workpiece deformation.
In addition, packing method can also be used. In order to increase the technological rigidity of the thin-walled workpiece, media can be filled in the workpiece to reduce the deformation of the workpiece during clamping and cutting. For example, the molten urea containing 3%~6% potassium nitrate is poured into the workpiece. After processing, the workpiece is immersed in water or alcohol, and the filler can be dissolved and poured out.

4. Reasonably arrange the process
During high-speed cutting, due to large machining allowance and intermittent cutting, the milling process often produces vibration, which affects the machining accuracy and surface roughness. Therefore, the NC high-speed machining process can generally be divided into: rough machining - semi-finish machining - corner cleaning - finish machining and other processes. For parts with high accuracy requirements, it is sometimes necessary to carry out secondary semi-finishing and then finish machining. After rough machining, the parts can be naturally cooled to eliminate the internal stress generated by rough machining and reduce deformation. The allowance left after rough machining shall be greater than the deformation, generally 1~2mm. During finishing, the finished surface of the part shall be kept with uniform machining allowance, generally 0.2~0.5mm, so that the tool is in a stable state during the processing, which can greatly reduce cutting deformation, obtain good surface processing quality and ensure the accuracy of the product.

Latest information

0755-32920268

免费1级a做爰片在线观看 | 中文字幕久久熟女人妻av免费 | 无码精品国产一区二区三区免费 | 国产日韩一区二区三区在线观看 | 亚洲精品午夜无码电影网 | 激情内射亚洲一区二区三区爱妻 | 国产在线aaa片一区二区99 | 色综合久久久久久久久五月 | 亚洲狠狠婷婷综合久久 | 98精品国产高清在线xxxx | 毛片国产精品完整版 | 两个黑人大战嫩白金发美女 | 久久综合亚洲色一区二区三区 | 蜜桃av抽搐高潮一区二区 | 国产成人精品午夜在线播放 | 四川少妇被弄到高潮 | 久久国产精品二国产精品 | 国产精品视频在 | 狠狠人妻久久久久久综合蜜桃 | 亚洲av无码一区二区二三区入口 | 日本三级片网站 | 乱色精品无码一区二区国产盗 | 欧美亚洲日韩国产人成在线播放 | 国产00高中生在线无套进入 | 国产女人在线视频 | 国模无码一区二区三区 | 4hu四虎永久免费地址ww416 | 午夜精品久久久久久毛片 | 国产精品美女久久久久久 | 国产啪精品视频网站 | 亚洲欧美日韩久久精品第一区 | 女人大荫蒂毛茸茸视频 | 69男女囗交动态图视频 | 久久人妻少妇嫩草av无码专区 | 1a级毛片免费观看 | 国产成人精品无码片区在线观看 | 老师脱了内裤让我进去 | 久久99精品国产99久久6男男 | 曰本女人牲交全视频免费播放 | 亚洲欧美中文日韩v在线观看 | 无码高潮爽到爆的喷水视频app |